Abstract
Bone is a continually regenerating tissue with the ability to heal after fractures, though healing significant damage requires intensive surgical treatment. In this study, borate-based 13-93B3 bioactive glass scaffolds were prepared though polymer foam replication and coated with a graphene-containing poly (ε-caprolactone) (PCL) layer to support bone repair and regeneration. The effects of graphene concentration (1, 3, 5, 10 wt%) on the healing of rat segmental femur defects were investigated in vivo using male Sprague–Dawley rats. Radiographic imaging, histopathological and immuno-histochemical (bone morphogenetic protein (BMP-2), smooth muscle actin (SMA), and alkaline phosphatase (ALP) examinations were performed 4 and 8 weeks after implantation. Results showed that after 8 weeks, both cartilage and bone formation were observed in all animal groups. Bone growth was significant starting from the 1 wt% graphene-coated bioactive glass-implanted group, and the highest amount of bone formation was seen in the group containing 10 wt% graphene (p < 0.001). Additionally, the presence of graphene nanoplatelets enhanced BMP-2, SMA and ALP levels compared to bare bioactive glass scaffolds. It was concluded that pristine graphene-coated bioactive glass scaffolds improve bone formation in rat femur defects.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.