Abstract
Bone formation around three types of fibrous calcium-containing crystals has been examined histologically using rats. The implanted materials are (i) calcium metaphosphate (beta-Ca(PO(3))(2)) fibers having aspect ratios of 15-80 with 2-20 microm in diameter, (ii) beta-Ca(PO(3))(2)) fibers surface-modified using dilute NaOH and (iii) calcium carbonate (CaCO(3); aragonite phase) whiskers having aspect ratios of 15-40 with 0.5-3 microm in diameter. Beta-Ca(PO(3))(2) fibers show a mechanically high strength with a low modulus of elasticity, and the surface-modified fibers have a thin layer consisting of a calcium orthophosphate phase. CaCO(3) whiskers were used for comparison reasons. The materials were implanted for 4, 8, and 12 weeks into bone defects created in the bone marrow of rat tibiae. Cancellous bone formation was observed around beta-Ca(PO3)2 fibers, the surface-modified fibers and CaCO(3) whiskers after implantation for 12, 4 and 4 weeks, respectively. CaCO(3) whiskers were scarcely observed after 12 weeks for resorbing. The calcium phosphate fibrous materials show combined advantages of mechanically high strength for toughening a matrix phase and biological activities; thus, these materials may prove to be useful for novel applications in the biomedical field.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of materials science. Materials in medicine
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.