Abstract
Orthodontic bands often fail clinically at the band-cement interface. Hybrid ionomer and resin cements and a glass ionomer control were bonded to photo-etched and standard band materials, both of which were tested in as-received and air-abraded conditions. Cements were placed in a 3 mm diameter mold at the bonding interface and bonded to 6 × 6 mm stainless steel band specimens mounted to acrylic blocks. Specimens were stored in water for 24 hours at 37°C and debonded in tension on a testing machine at 0.05 cm/minutes. Bond strengths (MPa) were calculated and data were analyzed by analysis of variance. Bond strengths to as-received bands were less than 3.4 MPa for cements tested, whereas bond strengths to air-abraded bands ranged from 7.1 to 17.7 MPa, except for the glass ionomer control. Air abrasion of band materials provides highly increased bond strength of hybrid ionomer and resin cements. (Am J Orthod Dentofacial Orthop 1999;115:143-7)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: American Journal of Orthodontics & Dentofacial Orthopedics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.