Abstract
Bonding characteristics of the metal and ceramic interfaces are significant to understand toughening mechanisms and design metal-ceramic composites. The Ni/alumina composite has been prepared by hot press-sintering of Ni-coated alumina powders and the bonding characteristics at the Ni-alumina composite interface have been studied by use of transmission electron microscopy (TEM)-based electron energy loss spectroscopy (EELS) techniques. From Al L2,3, Ni L2,3, and O K-edge EELS spectrum obtained, it can be reasoned that the interface in the Ni/alumina composite mainly consists of aluminum-terminated alumina and metallic Ni, and the bonding between them is primarily nonreactive with a nonionic ?Ni?Ni?Al?O?linkage, rather than by chemical bonding with Ni?O bonds from ?Ni?Ni?Ni?O?Al?O? or chemical reaction forming spinel interphases.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Materials and Structural Integrity
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.