Abstract
AbstractThe solid‐state batteries (SSBs) with Li anode present one of the most promising energy storage systems due to their enhanced energy density and safety. However, interfacial problems between Li anode and solid‐state electrolyte hinder the advancement of SSBs. Among them, insufficient solid‐solid interfacial contact is the main issue, which causes large resistance and hinders Li+ diffusion, leading to current distribution unevenness and lithium dendrites growth. To meet these challenges, a silver/carbon interlayer composed of ultrafine Ag nanoparticles (≈5 nm) grown on COOH‐CNTs (nano‐Ag@COOH‐CNTs) is constructed. In which, nano‐Ag is designed to guide homogeneous Li deposition, while CNTs substrate bonds with Li6.5La3Zr1.5Ta0.5O12 (LLZTO) electrolyte by reactions between ─COOH groups and LLZTO alkaline surface, thus transforming loose physical solid‐solid contact to chemical bonding contact. In addition, nano‐Ag is immobilized by CNTs, avoiding the migration of Li+ implanted nano‐Ag during cycling. Therefore, nano‐Ag@COOH‐CNTs interlayer can boost Li+ transport at LLZTO/Li interface and inhibit Li dendrites, achieving an ultra‐low interfacial resistance of 0.25 Ω cm2, a high critical current density of 1.7 mA cm−2 and a long cycling over 2155 h at 0.5 mA cm−2. The modified SSBs with LiNi0.83Co0.12Mn0.05O2 cathode cycles stably over 500 cycles. Moreover, high‐loading SSBs operate stably for 85 cycles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.