Bond strength and quality of bond interface of multifilament fiberglass posts luted onto flat-oval root canals without additional dentin wear after biomechanical preparation

Abstract

Statement of problemAn intraradicular retainer formed by multiple independent glass fiber filaments was developed aiming to allow better adaptation in flattened root canals; however, the performance of the new posts is unclear. PurposeThe purpose of this in vitro study was to compare the bond strength (BS) and adhesive interface quality achieved in flattened root canals restored with conventional glass fiber posts (CFPs) and multifilament glass fiber posts (MFPs). Material and methodsThe distal roots of mandibular molars with long oval root canals were endodontically treated, and the obturation material was removed and assigned to 2 groups (n=11) according to the type of retainer used: CFP (WhitePostDC#0.5; FGM) or MFP (CometTail#4; Synca). The posts were cemented with self-adhesive resin cement. The specimens were sectioned (2 slices per third). The most cervical slice in each third was used to evaluate the BS, while the adhesive interface in the apical slices was analyzed by scanning electron microscopy. BS data were analyzed by using a multilevel generalized linear model, and adhesive interface SEM data were analyzed by using a multilevel ordinal logistic regression model (α=.05). ResultsMultilevel regression showed a statistically significant difference for the “type of retainer” factor (P=.001; CFP 2.61 ±1.30>MFP 1.59 ±1.54). No statistically significant differences were found for the “root thirds” factor (P=.346) or for the interaction of both factors (P=.114). The failure pattern was predominantly mixed or adhesive for CFP and adhesive to dentin for MFP. A better adaptation of the restorative material was observed in the cervical third for CFP and in the apical third for MFP (P<.001). ConclusionsMFP resulted in lower BS values than CFP, with a higher prevalence of adhesive failures to dentin and better adaptation of the adhesive interface in the apical third.