Bond strength and interactions of machined titanium-based alloy with dental cements

Abstract

Statement of problemThe most appropriate luting agent for restoring cement-retained implant restorations has yet to be determined. Leachable chemicals from some types of cement designed for teeth may affect metal surfaces. PurposeThe purpose of this in vitro study was to evaluate the shear bond strength and interactions of machined titanium-based alloy with dental luting agents. Material and methodsEight dental luting agents representative of 4 different compositional classes (resin, polycarboxylate, glass ionomer, and zinc oxide-based cements) were used to evaluate their effect on machined titanium-6 aluminum-4 vanadium (Ti-6Al-4V) alloy surfaces. Ninety-six paired disks were cemented together (n=12). After incubation in a 37°C water bath for 7 days, the shear bond strength was measured with a universal testing machine (Instron) and a custom fixture with a crosshead speed of 5 mm/min. Differences were analyzed statistically with 1-way ANOVA and Tukey HSD tests (α=.05). The debonded surfaces of the Ti alloy disks were examined under a light microscope at ×10 magnification to record the failure pattern, and the representative specimens were observed under a scanning electron microscope. ResultsThe mean ±SD of shear failure loads ranged from 3.4 ±0.5 to 15.2 ±2.6 MPa. The retention provided by both polycarboxylate cements was significantly greater than that of all other groups (P<.05). The scanning electron microscope examination revealed surface pits only on the bonded surface cemented with the polycarboxylate cements. ConclusionsCementation with polycarboxylate cement obtained higher shear bond strength. Some chemical interactions occurred between the machined Ti-6Al-4V alloy surface and polycarboxylate cements during cementation.