Abstract
The aim of this in vitro investigation was to evaluate the effects of different dentin treatments on µTBS values of three different universal adhesives. Sixty extracted bovine incisors were used. The teeth were horizontally sectioned from the enamel-cement junction and embedded in an acrylic resin. Enamel was removed with 180-grit SiC paper to expose dentin. The exposed dentin surfaces were further polished with 600-grit SiC paper to provide a standardized smear layer. Teeth were randomly divided into three groups, according to the universal adhesives: All-Bond Universal, Single Bond Universal, and G-Bond Plus. Each group was then assigned into four subgroups, according to the dentin treatments: etch-and-rinse mode (ER), ER + 2% chlorhexidine (CHX), ER + %2.5 genipin (GE), and self-etch mode (SE). Samples were longitudinally sectioned across the bonded-interfaces to obtain resin-dentin beams. Beams were prepared from the same teeth were randomly and equally divided into two groups: immediate µTBS testing and µTBS testing after 6-month. The failure loads were recorded in MPa, and failure modes were evaluated at 30× magnification. The data were analyzed using a two-way ANOVA, to determine the effects of dentin treatment and storage time, and the interaction of these two factors on the µTBS of universal adhesives. Dentin treatments were showed significant differences (p < 0.05). ER mode exhibited higher µTBS than SE mode. However, universal adhesives were more durable in the SE mode than ER mode. Also, chlorhexidine treatment significantly improved adhesive performance of all universal adhesives, while no significant improvement was detected with genipin treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.