Abstract
The photoluminescent (PL) and electroluminescent (EL) characteristics in the thin films of various Bi-activated binary oxide phosphors have been investigated. La 2O 3:Bi, Gd 2O 3:Bi and Y 2O 3:Bi phosphor thin films were prepared on thick BaTiO 3 ceramic sheet substrates by r.f. magnetron sputtering depositions followed by postannealing. Intense blue PL emissions were observed from all Bi-activated binary oxide phosphor thin films postannealed at a high temperature. Blue, whitish blue-green or blue-green emissions were observed from thin-film electroluminescent (TFEL) devices fabricated with a La 2O 3:Bi, a Gd 2O 3:Bi or a Y 2O 3:Bi thin-film emitting layer, respectively. In addition, high luminance with good color purity in blue EL was obtained in a TFEL device using a La 2O 3:Bi thin film prepared under optimized conditions.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.