Abstract
Modified sonochemical route was used to prepare Y2O3:Tm3+ (1–11mol%) nanophosphor using Mimosa pudica (M.P.) leaves extract as bio-surfactant. The prepared samples were exhibited high crystalline nature with various morphologies. This was due to sonochemical experimental reaction took place between cavitation bubbles and nearby solution. The average crystallite sizes of the prepared samples were about 15nm to 21nm as obtained from PXRD and TEM analysis. The ultraviolet visible absorption spectra showed prominent bands with an energy gap varied from 5.73eV to 5.84eV. Photoluminescence (PL) emission spectra shows the prominent blue light emission peak at ~456nm attributed to 1D2→3F4 transitions of Tm3+ ions. Judd–Ofelt intensity parameters were estimated by using PL emission spectra. The photometric characteristics of the prepared compounds were very close to the blue color of NTSC standards. So the results were fruitful in making use of Y2O3:Tm3+ nanophosphor as an alternative material for effective blue component in WLED's.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.