Abstract
A black aluminum (B-Al) film was deposited onto the surface of a stack structure of platinum/Pb(ZrxTi1 − x)O3/platinum (Pt/PZT/Pt) to convert light into a heat variation and the heat variation into a polarization change. A comparison was performed between B-Al/Pt/PZT/Pt and conventional Pt/PZT/Pt structures. An absorbance higher than 95% was measured for the B-Al layer over a large range of wavelengths varying from 350 nm to 1000 nm. The theoretical model shows that heat diffusion was extremely fast through the layers, and the sample holder played a key role in the variation and stabilization of the system temperature. A doubled variation of the polarization was observed when the light was applied onto the surface of the stack structure with stable B-Al on the top. This behavior was interpreted by the larger temperature variations induced under the highly absorptive B-Al layers, in good correlation with the theoretical model prediction based on the heat fluxes in the structures. This result is very promising for possible pyroelectric energy harvesting applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.