Abstract
Amorphous magnetostrictive 50 μm diameter Fe <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">77.5</inf> Si <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">7.5</inf> B <inf xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">15</inf> wires exhibiting square and bistable hysteresis loops have been obtained by field-tension annealing and flash annealing treatments of cold-drawn as-quenched wires. Highest switching field, 1.3 Oe, and domain drive field, 0.5 Oe, for annealing temperature 330 C , time 30 min, axial tension 150 Kg/mm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> and axial field 200 Oe are an order of magnitude improvement over the as-quenched (AQ) state. Corresponding induced peak voltage is 0.5 mV/turn with exciting sinusoidal field 2 Oe and 60 Hz. Shorter pulse generation elements (≈ 2 cm) than for AQ wires (≈ 6 cm) were realized with 0.5 mV/turn peak voltage. Maximum squareness ratio is close to unity, twice that of AQ (125 μm) wires.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.