Abstract
Many contaminants in water are not completely removed by conventional water purification techniques. So, the need of fast and efficient technique for water purification is required for efficient removal. Photocatalysis using low bandgap semiconductors is capable of detoxifying contaminated water. Herein, bismuth sulfide (Bi2S3) nanorods were synthesized using a solid-state reaction method and their photocatalytic performance was tested for the removal of Congo red dye from water. X-ray diffraction (XRD) results confirmed the formation of Bi2S3 with a crystallite size of 5.0 nm. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images confirmed the formation of Bi2S3 nanorods with a diameter of 20–30 nm, length of 100 nm -150 nm and an aspect ratio of 5. Photoluminescence (PL) spectrum revealed the bandgap value of 2.47 eV. The specific surface area calculated using Brunauer–Emmett–Teller (BET) of Bi2S3 nanorods was 94.44 m2/g and pore volume was 0.158 cm3/g. The photodegradation of toxic Congo red was performed using Bi2S3 nanorods under UV irradiation. Photodegradation efficiencies up to 87% for Congo red dye were observed within 90 min. The pseudo-first-order (PFO) kinetic model was best fitted to understand the kinetics of photocatalysis. For Bi2S3 nanorods photocatalysts, the apparent rate constant value was 0.01573/min with a 0.997 correlation coefficient value.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.