Abstract
The aim of this paper was to synthesize and characterize microbial chitosan thin films for potential piezoelectric application. Microbial chitosan was derived from the Aspergillus oryzae fungus via extraction and deacetylation. Chitosan thin film was characterized for its surface morphology, chemical properties, tensile strength, and surface topography. For the potential application of chitosan as a piezoelectric material, its piezoelectric characteristics were presented in terms of its electromechanical coupling coefficient and piezoelectric coefficient. The fabrication of the chitosan thin films was optimized via the one-factor-at-a-time (OFAT) method, where the parameters were type of acid solvent, acid concentration and mixing time. The chitosan film prepared using formic acid at a concentration of 0.25 M for 3 h of mixing time had the highest tensile strength (129.29 MPa), electromechanical coupling factor (0.0045), and piezoelectric coefficient d31 (10 pC/N). The results obtained, from the optimized fabrication of the chitosan thin film, were validated against fungal chitosan, and it was shown that the properties of the thin film were comparable to those of commercial PVDF thin films. Therefore, the prospect of using microbial chitosan thin film as wearable piezoelectric energy harvester or nano-generator is promising.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.