Abstract
Thin and defect-free calcium phosphate films with a Ca/P ratio of 1.62 were formed by electron-beam evaporation. The as-deposited films had average bonding strengths to the metal implants of 64.8 MPa and the dissolution rates of 47.5 nm/h in isotonic saline solutions. The interface mechanical characteristics and histology of the as-machined, as-blasted, and calcium phosphate coating on the machined surfaces of commercially pure titanium were investigated. After a healing period of 12 weeks, the implants were unscrewed with a torque gauge instrument at the day of sacrifice. The coated sample showed a removal torque of 48.5 Ncm (SD 5.4) compared to 32.3 Ncm (SD 2.91) for the uncoated implant with the same surface roughness, and 47.3 Ncm (SD 5.8) for the grit blasted screw. The histomorphometric analyses of the calcium-phosphate-coated implants revealed a mean of 52.4% (SD 6.3) as the highest bone to implant contact.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.