Abstract
The use of MAPLE synthesized thin films based on BG and VD3 for improving the osseointegration and corrosion protection of Ti-like implant surfaces is reported. The distribution of chemical elements and functional groups was shown by FTIR spectrometry; the stoichiometry and chemical functional integrity of thin films after MAPLE deposition was preserved, optimal results being revealed especially for the BG+VD3_025 samples. The morphology and topography were examined by SEM and AFM, and revealed surfaces with many irregularities, favoring a good adhesion of cells. The thin films' cytotoxicity and biocompatibility were evaluated in vitro at the morphological, biochemical, and molecular level. Following incubation with HDF cells, BG57+VD3_ 025 thin films showed the best degree of biocompatibility, as illustrated by the viability assay values. According to the LDH investigation, all tested samples had higher values compared to the unstimulated cells. The evaluation of cell morphology was performed by fluorescence microscopy following cultivation of HDF cells on the obtained thin films. The cultivation of HDF's on the thin films did not induce major cellular changes. Cells cultured on the BG57+VD3_025 sample had similar morphology to that of unstimulated control cells. The inflammatory profile of human cells cultured on thin films obtained by MAPLE was analyzed by the ELISA technique. It was observed that the thin films did not change the pro- and anti-inflammatory profile of the HDF cells, the IL-6 and IL-10 levels being similar to those of the control sample. The wettability of the MAPLE thin films was investigated by the sessile drop method. A contact angle of 54.65° was measured for the sample coated with BG57+VD3_025. Electrochemical impedance spectroscopy gave a valuable insight into the electrochemical reactions occurring on the surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.