Biodegradability of Epoxidized Soybean Oil Based Thermosets in Compost Soil Environment

Abstract

In this study, bio-thermoset from epoxidized soybean oil (ESO) was prepared in the presence of methylhexahydrophthalic anhydride curing agent and 2-ethyl-4-methylimidazole catalyst. The crosslink densities of the synthesized ESO are ranged from 0.109 × 10−3 to 0.308 × 10−3 mol/cm3. The ESO bio-thermosets were exposed to the soil-burial test for 8 months. Weight change and morphology of the degraded ESO specimens were assessed. It was found that the weight loss of ESO was governed by the materials compositions, crosslink density and the soil-burial exposure time. The 3 mm thickness ESO bio-thermosets with crosslink density of 0.109 × 10−3 mol/cm3 had fully biodegraded after soil-burial for 6 months. In addition, 16S rDNA sequencing was carried out to identify the soil microorganisms. It was suggested that Comamonas sp., Bacillus sp., Streptomyces sp. and Acinetobacter sp. are the possible soil microbes that degrade the ESO bio-thermosets in the compost soil environment.