Abstract
This study was conducted to examine the effects of coating poly(D,L-lactide-co-glycolide) (PLGA)/recombinant human bone morphogenetic protein-2 (rhBMP-2) submicron particles by electrospray onto titanium (Ti) implants on the proliferation and differentiation capacity of mesenchymal stem cells. In addition, the duration of rhBMP-2 release was investigated. Ti disks were fabricated and divided into four groups as follows. Group C (control) was anodized at 300 V, group P was anodized and then coated with 0.2% PLGA, group B1 was anodized and then coated with PLGA/rhBMP-2 submicron particles at 200 ng per disk, and group B2 was anodized and then coated with PLGA/rhBMP-2 submicron particles at 600 ng per disk. The topography of the PLGA/rhBMP-2-coated Ti surfaces was examined, and proliferation assays, alkaline phosphatase activity tests, and rhBMP-2 releasing tests were conducted in vitro. There was no difference in the roughness of control Ti disks and Ti disks coated with PLGA/rhBMP-2 submicron particles by electrospray. The proliferation of mesenchymal stem cells increased over time; at 7 days, cell proliferation on the Ti disks coated with rhBMP-2 was significantly higher than the other groups. Anodized Ti disks coated with PLGA/rhBMP-2 (groups B1 and B2) released rhBMP-2 for approximately 21 days. In accordance with the amount of rhBMP-2 released from the PLGA/rhBMP-2 construct, the differentiation capacity of mesenchymal stem cells on the PLGA/rhBMP-2-coated disks was increased significantly. Submicron PLGA/rhBMP-2 coating on Ti implants by electrospray facilitated cell proliferation and differentiation, which is important for early healing and integration of implants.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: The International journal of oral & maxillofacial implants
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.