Bioceramics synthesis of hydroxyapatite from red snapper fish scales biowaste using wet chemical precipitation route

Abstract

Fish scales biowaste contain high collagens and calcium phosphates, therefore have considerable potential as raw material for value-added biomaterial such as hydroxyapatite (HAp). HAp is the main constituent component of hard tissue such as bone and teeth in the human body and is known as bioceramic materials. In this work, wet chemical precipitation method was used to syntesize HAp from Red Snapper Fish (Lutjanus campechanus) Scales. Two variations of calcination temperatures of 600°C (FHAp1) and 800°C (FHAp2) were conducted for 5 hours. The results showed calcium content from biowaste of red snapper fish scale was 83.62%. FTIR result shows that PO43-, OH-, and CO32- functional groups presence as indicates the formation of HAp. XRD result showed the degree of crystallinity for FHAp1 and FHAp2 were 75.52% and 79.20%, respectively. The degree of crystallinity is in accordance with ISO 13779-2:2000 standard in which the minimum degree of crystallinity of hydroxyapatite used for biomedical materials is 45%. Finally, Particle Size Analyzer (PSA) results show that the particle size distribution is evenly distributed, with the size of micro-scale hydroxyapatite particles, ranging from 5.76 μm to 132.64 μm.