Abstract
Diamond-particle-dispersed aluminum (Al) matrix composites consisting of monomodal and bimodal diamond particles were fabricated in spark plasma sintering process, where the mixture of diamond, pure Al and Al-5mass% Si alloy powders were consolidated in liquid and solid co-existent state. Microstructures and thermal properties of the composites fabricated in such a unique way were investigated and the bimodal and monomodal diamond particle effect was evaluated on the thermal properties of the composites. The composites can be well consolidated in a temperature range between 773 K and 878 K and scanning electron microscopy detects no reaction product at the interface between the diamond particle and the Al matrix. Relative packing density of the composite containing monomodal diamond particles decreased from 99.1% to 87.4% with increasing volume fraction of diamond between 50% and 60%, whereas that of the composite containing bimodal diamond particles was higher than 99% in a volume fraction of diamond up to 65%. The thermal conductivity of the composite containing bimodal diamond particles was higher than that of the composite containing monomodal diamond particles in a volume fraction of diamond higher than 60% and the thermal conductivity of the composite containing 70 vol.% bimodal diamond particles was 578 W/mK at R.T..
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.