Abstract
The new system of (BNKLT-x/y) lead-free piezoelectric ceramics, which were prepared by using conventional oxide mixing processing, were invented in our group. The ceramics show excellent piezoelectric and ferroelectric properties: d 33 =231 pC/N, k p =41.0 00, k t =50.5 %, P r =40.2 ?C/cm2, and E c =2.47 kV/mm, respectively. The dependence of P-E loops on temperature reveals that the depolarization temperature T d of BNKLT-0.15/0.075 ceramics, which simultaneously have good piezoelectric properties (d 33 =164 pC/N, k p =36.3%, k t =48.6 %) and strong ferroelectricity (P r =38.8 ? C/cm2, E c =3.73 kV/mm) at room temperature, is about 195 °C. The ceramics were used for making buzzers by ordinary techniques as used for PZT-based buzzers, and the measurement of the electric-acoustic properties shows that the buzzers possess a very high sound pressure (90 dB). The ceramics invented were also used for making middle frequency piezoelectric ceramic filters.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.