Abstract
Bifunctional hydrogel materials having both fouling resistance and antimicrobial activity were prepared by the photopolymerization of polyethylene glycol diacrylate (PEGDA) and a functional monomer containing ammonium salt (RNH 3Cl) in the presence of a photoinitiator. Water was added to the prepolymerization mixture to increase the solubility of the RNH 3Cl monomer and to control the cross-linking density of the UV-cured films. The water uptake and permeability of the resulting films were easily controlled by manipulating the composition ratio of the PEGDA and RNH 3Cl monomers and by varying the water content in the prepolymerization mixture. Extremely high water uptake (up to 900%) and permeability (∼200 L μm m −2 h −1 atm −1 or above) values were observed for the films prepared by adding 80% (w/w) water into the prepolymerization mixtures of PEGDA and RNH 3Cl (weight ratio = 1:1 or 2:1). PSF UF membranes coated with these water-absorbing hydrogel materials showed excellent anti-fouling efficiency in cross-flow filtration tested using an oil–water emulsion or a bovine serum albumin (BSA) solution as the feed. Antimicrobial activity of the hydrogel materials was also demonstrated by a case study employing E. coli.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.