Abstract
Niobium doped indium tin oxide (ITO:Nb) thin films were fabricated on glass substrates by RF magnetron sputtering from one piece of ceramic target material at room temperature. The bias voltage dependence of properties of the ITO:Nb films were investigated by adjusting the bias voltage. Structural, electrical and optical properties of the films were investigated using X-ray diffraction (XRD), atomic force microscopy (AFM), UV–visible spectroscopy, and electrical measurements. XRD patterns showed a change in the preferential orientations of polycrystalline crystalline structure from (222) to (400) crystal plane with the increase of negative bias voltage. AFM analysis revealed that the smooth film was obtained at a negative bias voltage of -120V. The root mean square (RMS) roughness and the average roughness are 1.37nm and 1.77nm, respectively. The films with the lowest resistivity as low as 1.45×10−4Ωcm and transmittance over 88% have been obtained at a negative bias voltage of −120V. Band gap energy of the films, depends on substrate temperature, varied from 3.56eV to 3.62eV.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.