Abstract
Bismuth ruthenate pyrochlore (Bi2Ru2O7: BRO) was tested as a cathode in several bismuth oxide-based electrolyte cells. Erbium oxide stabilized bismuth oxide (ESB) (Bi2O3)0.8 (Er2O3) 0.2, Bi2V0.9Me0.1O5.35 (BIMEVOX10, Me = Co, Cu, Zn), and Bi2Ru2O7 (BRO) were synthesized via solid state reaction. ESB and BIMEVOX powders were pressed and sintered into dense pellets while BRO was deposited and sintered as porous electrodes onto ESB and BIMEVOX dense pellet surfaces. Morphologies and phases of the materials were characterized by Field Emission Scanning Electron Microscope and x-ray diffraction, respectively. Electrochemical performances of BRO/ESB and BRO/BIMEVOX symmetric cells were tested using Electrochemical Impedance Spectroscopy (EIS) at 200-700 {degree sign}C in air. High polarization for BIMEVOX cells was observed, while ESB cells showed a promising behaviour. Different electrochemical performances of BRO electrodes, with ESB or BIMEVOX, indicated that the phases formed at electrodes/electrolyte interface controlled the cell polarization process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.