Bi2 Te3 /Bi2 Se3 /Bi2 S3 Cascade Heterostructure for Fast-Response and High-Photoresponsivity Photodetector and High-Efficiency Water Splitting with a Small Bias Voltage.

Abstract

Large-scale multi-heterostructure and optimal band alignment are significantly challenging but vital for photoelectrochemical (PEC)-type photodetector and water splitting. Herein, the centimeter-scale bismuth chalcogenides-based cascade heterostructure is successfully synthesized by a sequential vapor phase deposition method. The multi-staggered band alignment of Bi2 Te3 /Bi2 Se3 /Bi2 S3 is optimized and verified by X-ray photoelectron spectroscopy. The PEC photodetectors based on these cascade heterostructures demonstrate the highest photoresponsivity (103mAW-1 at -0.1V and 3.5mAW-1 at 0V under 475nm light excitation) among the previous reports based on two-dimensional materials and related heterostructures. Furthermore, the photodetectors display a fast response (≈8ms), a high detectivity (8.96×109 Jones), a high external quantum efficiency (26.17%), and a high incident photon-to-current efficiency (27.04%) at 475nm. Due to the rapid charge transport and efficient light absorption, the Bi2 Te3 /Bi2 Se3 /Bi2 S3 cascade heterostructure demonstrates a highly efficient hydrogen production rate (≈0.416mmolcm-2 h-1 and ≈14.320µmolcm-2 h-1 with or without sacrificial agent, respectively), which is far superior to those of pure bismuth chalcogenides and its type-II heterostructures. The large-scale cascade heterostructure offers an innovative method to improve the performance of optoelectronic devices in the future.