Abstract
The microstructure, mechanical properties and corrosion resistance of 30Cr13 martensitic stainless steel (MSS) with different Nb contents were investigated by using the optical microscope, scanning electron microscope, X-ray diffractometer, HRC hardness measurement apparatus and tensile testing machine. Nb was found to retard the formation of austenite and promote the precipitation of carbides by calculating. The results showed that the addition of 0.2 wt.% Nb elements could improve the strength and corrosion resistance of 30Cr13 martensitic stainless steels while the reduction in toughness was less because of the inhibited effect on Cr-rich carbides precipitation by Nb addition. Specially, M23C6-type carbides almost disappeared in 0.6Nb-MSS. Moreover, the main existent form of Nb element was NbC and the strong carbide-forming ability of Nb element increased the quantity of carbides with the morphology changing from spherical-type to chain-type. 0.2Nb-MSS shows excellent strength, adequate toughness and sufficient corrosion resistance for the application.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
More From: Journal of Iron and Steel Research International
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.