Abstract
Fine grained and dense dielectric ceramics of the BaO-Nd2O3-TiO2 system have been fabricated by the most advanced Spark Plasma Sintering (SPS) technology, whose average grain size is about 100nm as determined by SEM. XRD showed that the diffractive peak of the sample was broadened clearly. The nano-ceramic microstructure formed by SPS is due to the high pressure up to 50 MPa, low temperature (1000°C) and fast sintering (1 minute). The BaO-Nd2O3-TiO2 ternary nanoceramic sample, which consists of the main phase Nd2Ti2O7 with perovskite-like layer structure (PLS) and the secondary phase BaNd2Ti4O12（Ba4.5Nd9Ti18O54）with perovskite-like tungsten bronze structure, was prepared for the first time by rapidly sintering nano-particles of the xBaO×(0.35-x)Nd2O3×0.65TiO2 compound. Those two phases are formed in BaO-Nd2O3-TiO2 micron-grained ceramics prepared by normal sintering of the nano-particles at 1300°C, resulting in good dielectric characteristics for microwave ceramics; however, dielectric characteristics are significantly degraded in the SPS-sintered samples probably due to the carbon contamination from the graphite SPS dies.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.