Abstract
In this study, occurence of failure after the interaction between an armour piercing 7.62 mm caliber projectile and a tempered bainitic steel has been investigated. The shot was performed at zero degree with a projectile velocity of 840 m/s. After the shot, microstructural and fractographical examinations were carried out on the sample taken from the perforated region. In the etched sample, it was observed that the morphology of the original microstructure had changed and adiabatic shear bands (ASBs) were formed in regions close to the direction of penetration. Main failure is ductile (plastic) deformation was followed by cleavage after shot. Cracks due to adiabatic shear band and formation of abrasive wear were seen. The perforation mode of the steel was a typical petalling.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.