Abstract
It has been well established that lead-free solder underperforms conventional leaded solder in reliability under dynamic impact. Common failures observed on ball-grid-array (BGA) solder balls on chip under board level impact include bulk solder ductile failure, intermetallic (IMC) layer crack and pad-lift. In this work, a finite element modeling approach was proposed to model bulk solder ductile failure and intermetallic layer crack. The use of beam elements and connector elements to represent the bulk solders and board/component side intermetallic layers, respectively, offers the advantage of simplicity over the use of continuum elements and cohesive elements for solder joints. This approach enables the modeling of assembly level impact with significantly less computational resources. The model was verified by comparing its prediction of BGA solder reliability against actual test results in a dynamic four-point bend test. The physical tests consist of ball impact at varying heights on a board with a mounted chip, and the subsequent analysis of the failure modes of the BGA solder joints. Simulation results were in good agreement with test results. The study shows that it is feasible to model BGA solder joint ductile failure and intermetallic layer crack under impact with simple elements with reasonable accuracy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.