Abstract
In this work, the non-destructive ball indentation technique is applied to estimate fracture toughness for three types of high-strength rail steels based on continuum damage mechanics. Damage parameter, in terms of the deterioration of elastic modulus, is measured for three rail steels using the loading-unloading smooth tensile test, based on which a ductile damage model is calibrated to determine the critical damage parameter at the onset of fracture. Meanwhile, an instrumented ball indentation test is conducted on the three rail steels to generate damage as a function of contact depth under indentation compression. The critical damage parameter from the smooth specimen is then applied to the indentation test to determine the critical contact depth for calculating the indentation fracture toughness based on the concept of indentation energy to fracture. Results show that although the magnitude of the so-determined indentation fracture toughness is greater than that of the corresponding mode I critical stress intensity factor (KIc) measured using the pre-cracked single-edge-notched bend (SENB) specimen, the former can well predict the ranking order of the KIc values among the three rail steels.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.