Autogenous healing and reinforcement corrosion of water-penetrated separation cracks in reinforced concrete

Abstract

Depending on the crack width, the thickness of the structure, the water pressure, and the degree of acid of the water, long-term investigations have been performed over a period of 2 years with respect to the autogenous healing and reinforcement corrosion of water-penetrated separation cracks in reinforced concrete by the University of Kaiserslautern, supported by the Deutsche Forschungsgemeinschaft (DFG). For the waters penetrating the cracks deionised water (neutral, pH=7.0), and boric acid treated deionised water with a pH-value of 6.1 and 5.2 (weakly acid waters) were used. A complete autogenous healing could not be observed. The water penetrating the cracks could hardly be measured with a pH-value of 7.0 at the end of the test. While naturally at the beginning of the test, no influence of the water-chemical degree of the acids could be determined, the existing flow-through quantities towards the end of the test period depended clearly on the crack width and the pH-value. With an increasing crack width and an increasing acid-degree larger flow-through quantities were measured. Depending on the pH-value and the crack width it was determined whether and to which extent corrosion developed at the reinforcing steel bars crossing the cracks. With a crack width of 0.1 mm, corrosion was not to be observed in any case. For the test specimens with a crack width of 0.2 mm a start of the corrosion was found depending on the pH-value. With an increasing width of the crack, an increasing corrosion development is to be expected for test specimens penetrated by acid water. For a crack width of 0.4 mm and a pH-value of 5.2, the highest corrosion development was to be observed, however, there were weakenings of the cross section not worth being mentioned even after a 2-year test period.