Abstract
In this study, novel AuPd bimetallic co-catalyst decorated Cd0.5Zn0.5S photocatalyst was successfully synthesized via an in-situ chemical deposition method. The physical as well as the photophysical properties of the as-obtained AuPd/Cd0.5Zn0.5S samples were characterized by X-ray diffractometry (XRD), Transmission electron microscope (TEM), UV–vis diffuse reflection spectroscopy (DRS), X-ray photoelectron spectroscopy (XPS) and surface photovoltage spectroscopy (SPV). The AuPd bimetallic co-catalysts showed dramatic photo-generated charge separation efficiency in Cd0.5Zn0.5S sample, and thus significantly enhance the H2 production activity under visible light irradiation. The AuPd/Cd0.5Zn0.5S sample with 0.5 wt% content had the highest catalytic activity, and the corresponding H2 evolution rate is 3.65 mmol g−1 h−1, which was about 12 times as that of pure Cd0.5Zn0.5S sample under visible light irradiation. The photocatalytic activity of the photocatalyst was stable even after 9 cycling photocatalytic experiments. A possible mechanism on the photocatalytic enhancement of AuPd NPs was systematically investigated, which can provide a novel concept for the synthesis of other desirable photocatalytic materials.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.