Au–Pd/3DOM Co3O4: Highly active and stable nanocatalysts for toluene oxidation

Abstract

The polymethyl methacrylate-templating and polyvinyl alcohol-protected reduction routes were adopted to prepared three-dimensionally ordered macroporous (3DOM) Co3O4 and its supported gold–palladium alloy (xAuPd/3DOM Co3O4, x=0.50–1.99wt% and Au/Pd mass ratio=1:1) nanocatalysts. The 3DOM Co3O4 supported Au–Pd samples performed much better than supported single Au or Pd samples, with the 1.99AuPd/3DOM Co3O4 sample showing the best performance: the T10%, T50%, and T90% (temperatures required for achieving toluene conversions of 10%, 50%, and 90%) were 145, 164, and 168°C at a space velocity of 40,000mL/(gh), respectively. The 3DOM Co3O4 supported Au–Pd nanocatalysts also exhibited better catalytic stability and more moisture-tolerant ability than the supported Au or Pd samples for toluene oxidation. The apparent activation energies (33–41kJ/mol) over xAuPd/3DOM Co3O4 were much lower than those (52–112kJ/mol) over 3DOM Co3O4 and supported single Au or Pd samples, with the 1.99AuPd/3DOM Co3O4 sample exhibiting the lowest apparent activation energy (33kJ/mol). It is concluded that better oxygen activation ability and stronger noble metal–3DOM Co3O4 interaction were responsible for the excellent catalytic performance of 1.99AuPd/3DOM Co3O4.