Abstract
This study employed 7 weight percent (wt.%) of untreated and treated MgO nanofillers incorporated into PVDF polymer. The effects of coupling agents (chlorotrimethylsilane and triacetoxyvinylsilane) on the polymorphism of PVDF/MgO nanocomposite were investigated. The PVDF/MgO nanocomposite thin films of untreated and treated MgO nanofillers, with and without the addition of coupling agents were produced via spin coating technique. The average thickness recorded for these films was 300 nm thick. ATR-FTIR was conducted to investigate the changes in polymorphism of PVDF/MgO nanocomposite thin films. The results shows that PVDF/MgO (Chlorotriemethylvinylsilane) indicates better compatibility than PVDF/MgO, with sharp and distinguished absorption band at 840 cm-1, indicating high content of PVDF, β-crystals.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.