Abstract
Nanocrystalline Mg was sputter deposited onto an Ar ion etched Si {100} substrate. Despite an ∼6 nm amorphous layer found at the interface, the Mg thin film exhibits a sharp basal-plane texture enabled by surface energy minimization. The columnar grains have abundant 〈0001〉 tilt grain boundaries in between, most of which are symmetric with various misorientation angles. Up to ∼20° tilt angle, they are composed of arrays of equally-spaced edge dislocations. Ga atoms were introduced from focused ion beam milling and found to segregate at grain boundaries and preferentially decorate the dislocation cores. Most symmetric grain boundaries are type-1, whose boundary planes have smaller dihedral angles with {21̄1̄0} rather than {101̄0}. Atomistic simulations further demonstrate that type-2 grain boundaries, having boundary planes at smaller dihedral angles with {101̄0}, are composed of denser dislocation arrays and hence have higher formation energy than their type-1 counterparts. The finding correlates well with the dominance of type-1 grain boundaries observed in the Mg thin film.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.