Abstract
Triangular nanovoids in 2D materials transition metal dichalcogenides have vertex points that cause stress concentration and lead to sharp crack propagation and failure. Here, the atomistic mechanics of back folding around triangular nanovoids in monolayer WS2 sheets is examined. Combining atomic-resolution images from annular dark-field scanning transmission electron microscopy with reactive molecular modelling, it is revealed that the folding edge formation has statistical preferences under geometric conditions based on the orientation mismatch. It is further investigated how loading directions and strong interlayer friction, interplay with WS2 lattice's crack preference, govern the deformation and fracture pattern around folding edges. These results provide fundamental insights into the combination of fracture and folding in flexible monolayer crystals and the resultant Moiré lattices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.