Abstract
Oxidation phenomena on metal surfaces can be advanced using atomistic modeling for the study of the structure and properties of the growing oxide films. Molecular dynamics investigations were performed to study thermal oxidation of single-crystal and polycrystalline Al–Mg alloys with low Mg content of up to 2.5 at. %. Structure, topological atom network and surface topography of the oxide films grown on Al–Mg surfaces at 300, 475 and 663 K are determined. Mg-content and temperature dependent oxide films developed on Al-Mg alloy substrates with two-phase oxide film formation as also confirmed experimentally. It is related with a gradual long-range order formation above 475 K for (Al,Mg)-oxide films, for which solid amorphous phase predominates over crystalline phase. The 1.12-nm-thick oxide films grown at 300 K are fully amorphous and build up from (Al, Mg)-oxide which the Al2O3 dominates. Increase of Mg coefficient confirms faster Mg diffusion to oxide/alloy interface at high oxidation temperature and the formation of MgO-like network. The presence of planar crystal defect (grain boundary, GB) into Al-Mg alloy substrate governs the kinetics of oxide film growth and its structure evolution. GB also compensate internal stresses during oxide film growth. Obtained results are in good agreement with experimental observations.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.