Atomically Thin Oxyhalide Solar-Blind Photodetectors.

Abstract

2D wide-bandgap semiconductors demonstrate great potential in fabricating solar-blind ultraviolet (SBUV) photodetectors. However, the low responsivity of 2D solar-blind photodetectors still limits their practical applications. Here, high-responsivity solar-blind photodetectors are achieved based on 2D bismuth oxychloride (BiOCl) flakes. The 2D BiOCl photodetectors exhibit a responsivity up to 35.7 A W-1 and a specific detectivity of 2.2 × 1010 Jones under 250 nm illumination with 17.8 µW cm-2 power density. In particular, the enhanced photodetective performances are demonstrated in BiOCl photodetectors with increasing ambient temperature. Surprisingly, their responsivity can reach 2060 A W-1 at 450 K under solar-blind light illumination, maybe owing to the formation of defective BiOCl grains evidenced by in situ transmission electron microscopy. The high responsivity throughout the solar-blind range indicates that 2D BiOCl is a promising candidate for SBUV detection.