Abstract
Technology to atomically flatten the silicon surface on (100) orientation large-diameter wafer and the formation technology of an atomically flat insulator film/silicon interface are developed in this paper. Atomically flat silicon surfaces composed of atomic terraces and steps are obtained on (100) orientation 200-mm-diameter wafers by annealing in pure argon ambience at 1200 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">deg</sup> C for 30 min. Atomically flat surfaces with various terrace widths and step structures are observed by atomic force microscopy. It is found that the atomic terrace width changes widely with an off angle of the wafer surface from the (100) lattice plane. It is also found that the direction of the off angle significantly affects the atomically flat surface morphology, i.e., when the directions of the off angles are parallel to the <110> directions, the step structure is composed of alternating pairs of straight and triangular steps. When the directions of the off angles are parallel to the <100> directions, the step structure is composed of only straight steps. By precise control of the off angle and the direction toward the <100> directions for a 200-mm-diameter silicon wafer, we have succeeded in fabricating an atomically flat surface with straight atomic steps and a very uniform terrace width of 140-150 nm on the entire surface of a large-diameter silicon wafer. Furthermore, it is found that only radical-reaction-based insulator film formation technology, such as oxidation utilizing oxygen radicals carried out at a low temperature (400 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">deg</sup> C ), preserves the atomic flatness of the insulator film/silicon interface. Finally, when MOSFETs are fabricated with an atomically flat interface, they exhibit near ideal subthreshold swing factors, with much smaller fluctuation, extremely lower 1/ <i xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">f</i> noise, and higher MOS dielectric breakdown field intensity compared with MOSFETs fabricated with conventional technologies.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.