Abstract
The microstructures of precipitates in Al–Zn–Mg alloys in peak-aged condition have been studied using scanning transmission electron microscope. The same thermo-mechanical treatment was applied in all alloys. Investigation of peak-aged samples revealed that the most commonly found phases were η′ and η 1 with their respective habit planes on {111}Al and {100}Al. η′ phases under [110]Al were analyzed and compared with η′ structure models. Furthermore, a close inspection of η 1 phase as the second most found precipitate revealed that it incorporates an anti-phase resembling boundary, not observed in other orientation relationships that precipitates create with Al matrix, in addition, differences in matrix-precipitate interfaces between η′/η 2 and η 1 phases were noticed. This paper addresses the first part to the analysis of η′ phase. Next part is extended to the analysis of the η 1 phase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.