Abstract
Atom probe tomography was employed to characterize the microstructure and C distribution in the white etching area (WEA) of a martensitic 100Cr6 bearing steel subjected to rolling contact fatigue. Different from its surrounding matrix where a plate-like martensitic structure prevails, the WEA exhibits equiaxed grains with a uniform grain size of about 10nm. Significant C grain boundary enrichment (>7.5at.%) and an overall higher C concentration than the nominal value are observed in the WEA. These results suggest that the formation of WEA results from severe local plastic deformation that causes dissolution of carbides and the redistribution of C.