Atomic retention and near infrared photoluminescence from PbSe nanocrystals fabricated by sequential ion implantation and electron beam annealing

Abstract

Nanocrystals of PbSe have been fabricated in a silicon dioxide matrix by sequential low energy ion implantation followed by an electron beam annealing step. Transmission electron microscopy reveals PbSe nanocrystals with typical sizes between 3 and 10nm in the sub-surface region. Rutherford Backscattering Spectrometry has been used to study the total atomic retention, as a function of implanted atoms, following annealing. Photoluminescence was observed in various samples, at 4K, as a broad peak between 1.4 and 2.0μm, with observation of a dependence of the peak wavelength on annealing temperature. Room temperature photoluminescence was observed for samples with a high retention of implanted atoms, demonstrating the importance of nanocrystal density for achieving ambient temperature emission in these systems.