Abstract
ABSTRACTTransmission electron microcopy (TEM) in both the parallel illumination and scanning probe mode revealed atomically ordered entities within a 5 to 250 nm range in a IV-VI and a II-VI compound semiconductor quantum dot (QD) system. While the II-VI system was a nominal [001] CdSe/(Mn0.1Zn0.9)Se multilayer structure with the QDs embedded, the IV-VI system nominally consisted of [111] PbSe islands. The comparison of photoluminescence (PL) spectra from the CdSe/(Mn0.1Zn0.9)Se structure with those of a reference structure, that was grown to the same nominal specification under otherwise identical conditions except that no Mn was incorporated into the cladding layers, revealed for the former sample two peaks at approximately 2 and 2.1 eV. We tentatively attribute these two PL peaks to two groups of atomically ordered entities.
Submitted Version (
Free)
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.