Atomic layer deposition of photoactive CoO/SrTiO3 and CoO/TiO2 on Si(001) for visible light driven photoelectrochemical water oxidation

Abstract

Cobalt oxide (CoO) films are grown epitaxially on Si(001) by atomic layer deposition (ALD) using a thin (1.6 nm) buffer layer of strontium titanate (STO) grown by molecular beam epitaxy. The ALD growth of CoO films is done at low temperature (170–180 °C), using cobalt bis(diisopropylacetamidinate) and water as co-reactants. Reflection high-energy electron diffraction, X-ray diffraction, and cross-sectional scanning transmission electron microscopy are performed to characterize the crystalline structure of the films. The CoO films are found to be crystalline as-deposited even at the low growth temperature with no evidence of Co diffusion into Si. The STO-buffered Si (001) is used as a template for ALD growth of relatively thicker epitaxial STO and TiO2 films. Epitaxial and polycrystalline CoO films are then grown by ALD on the STO and TiO2 layers, respectively, creating thin-film heterostructures for photoelectrochemical testing. Both types of heterostructures, CoO/STO/Si and CoO/TiO2/STO/Si, demonstrate water photooxidation activity under visible light illumination. In-situ X-ray photoelectron spectroscopy is used to measure the band alignment of the two heterojunctions, CoO/STO and CoO/TiO2. The experimental band alignment is compared to electronic structure calculations using density functional theory.