Abstract
Niobium carbide thin films were synthesized by atomic layer deposition (ALD) using trimethylaluminum (TMA), NbF5, and NbCl5 precursors. In situ quartz crystal microbalance (QCM) measurements performed at 200 and 290 °C revealed controlled, linear deposition with a high growth rate of 5.7 and 4.5 A/cycle, respectively. The chemical composition, growth rate, structure, and electronic properties of the films were studied over the deposition temperature range 125–350 °C. Varying amounts of impurities, including amorphous carbon (a-C), AlF3, NbFx, and NbClx, were found in all samples. A strong growth temperature dependence of film composition, growth rate, and room temperature DC resistivity was observed. Increasing film density, decreasing total impurity concentration, and decreasing resistivity were observed as a function of increasing deposition temperature for films grown with either NbF5 or NbCl5. Superconducting quantum interference device (SQUID) magnetometry measurements down to 1.2 K revealed a superc...
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.