Abstract
AbstractThe surface of cellulose triacetate (CTA) film was modified with gaseous plasma of several discharge power in the presence of Argon (Ar) gas at 0.5 torr pressure. After gas plasma etching, the surface structure of the films is analyzed by atomic force microscopy (AFM) and measured with peel strength. Furthermore, the wetting properties of the CTA film treated with Ar plasma are studied by contact angle measurement. Peel strength after plasma treatment was increased with increasing plasma treatment time. However, treatments of plasma greater than 7 min did not find an additional increase in peel strength, similarly to roughness and morphological changes of AFM. The water contact angle decreased for an initial treatment time due to the improved wettability of the film, but showed an increasing trend for a higher treatment time (7 min). These results show that Ar plasma treatment is a convenient tool for improving the adhesive properties of CTA film. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 3963–3971, 2006
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.