Abstract
The aim of this study was to evaluate, through Raman spectroscopy, the repair of complete tibial fracture in rabbits fixed with wire osteosynthesis - WO, treated or not with infrared laser light (λ 780nm, 50mW, CW) associated or not to the use of HATCP and GBR. Surgical fractures were created under general anesthesia (Ketamine 0.4ml/Kg IP and Xilazine 0.2ml/Kg IP), on the tibia of 15 rabbits that were divided into 5 groups and maintained on individual cages, at day/night cycle, fed with solid laboratory pelted diet and had water ad libidum. On groups II, III, IV and V the fracture was fixed with WO. Animals of groups III and V were grafted with hydroxyapatite + GBR technique. Animals of groups IV and V were irradiated at every other day during two weeks (16J/cm2, 4 x 4J/cm2). Observation time was that of 30 days. After animal death the specimens were kept in liquid nitrogen for further analysis by Raman spectroscopy. Raman spectroscopy showed significant differences between groups (p<0.001). It is concluded that IR laser light was able to accelerate fracture healing and the association with HATCP and GBR resulted on increased deposition of calcium hydroxyapatite.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.