Abstract
This paper reports Surface treatment of nano alumina with vinyl silane coupling agents was performed. Modification with silane coupling agents is commonly method by which the interfacial interaction of particles can be enhanced with resin. Surface treatment of nano alumina was implement under hydrolysis and condensation condition at different silane concentration. The surface characteristics of the unmodified and modified aluminum pigments were investigated by means of CH and FTIR analyses. The Mechanical properties of vinyl ester resin was investigated by the Dynamic mechanical thermal Analysis (DMTA). Results revealed that vinyl silane adsorbed on the surface of alumina under sol-gel reaction. Also, the mechanical properties of the vinyl ester composite was significantly enhanced with surface treated particles.
Highlights
In this study Surface treatment of nano alumina with vinyl silane coupling agents was performed
Modification with silane coupling agents is commonly method by which the interfacial interaction of particles can be enhanced with resins
Surface treatment of nano alumina was implement under hydrolysis and condensation condition at different silane concentration
Summary
In this study Surface treatment of nano alumina with vinyl silane coupling agents was performed. Surface treatment of nano alumina was implement under hydrolysis and condensation condition at different silane concentration. The present work is an attempt to study the interfacial bonding strength between differently vinyl silane treated nano Alumina and a vinyl ester matrix. According to Eq (1), it can be seen that the lowest amount of silane needed for surface modification of 5 gr nanoparticles is 0.24 gr.