Abstract
The properties of eco-composite boards from agro-waste of oil palm empty fruit bunches were studied. The oil palm empty fruit bunches (EFB) obtained from a private oil palm plantation. By using fibre cutter and particle crusher, these EFB refined. Hardeners and wax added at 1% and 3% during the mixing process. Boards with densities of 500, 600 and 700 kg/m3 produced using resin urea formaldehyde as the bonding agent at 10, 12 and 14%. The boards conditioned in a conditioning chamber set at 20±2 °C and 65% relative humidity before undergoing subsequent testing. The EN Standards specifications applied in the preparation of test samples and testing. Results showed the highest modulus of rupture (MOR) and modulus of elasticity (MOE) achieved in this study were 22.91 N/mm2 and 2059.56 N/mm2. The internal bonding was found to be at 0.98 N/mm2, and 467.47 N/mm2 and 512.37 N/mm2 respectively for the edge and face screw withdrawal. Boards with 700 kg/m3 density and 14% resin content met the requirement of standard specifications. Scanning electron microscopy machine used to study the resin-fibre bonding property. Resin and fibre in the board inspected carefully, and voids appeared at the cross-section of the board with density 500 kg/m3 at 10% resin suggesting moisture penetrated into the board via the open spaces and weakened the linkages existed, thus cause the board to have low properties. The thermogravimetric analysis indicates maximum rate of decomposition for the EFB boards occurred at 380.83 °C. This study shows that the board’s density and resin content applied influence on the board’s overall properties with boards produced at 700 kg/m3 density with 14% resin content showed excellent overall properties with good dimensional stability.
Highlights
The timber industry has started slowly to turn to wood composite as an alternative to the use of natural timber
empty fruit bunches (EFB) are available in abundance in Malaysia, converting them into composite boards can be a way to resolve the scarcity of wood sources in the tropical region of the world where the plants grow
The present study focuses on assessing the suitability of using agro-waste from oil palm empty fruit bunches as quality eco-composite boards
Summary
The timber industry has started slowly to turn to wood composite as an alternative to the use of natural timber. An enormous amount of oil palm biomass becomes available during this period. This biomass usually left to rot in the fields. This readily available renewable resource could be used as a raw material for wood-based industry (Rasat et al, 2013b, 2013c, 2013e). EFB are available in abundance in Malaysia, converting them into composite boards can be a way to resolve the scarcity of wood sources in the tropical region of the world where the plants grow