Aspects of intrinsic coercivity via Gd analogs

Abstract

Some aspects of intrinsic coercivity in rare earth-transition metal compounds series are discussed with emphasis on comparison of relevant parameters between series based on Gd with analogs based on anisotropic rare earths. In particular the lack of low temperature coercivity in GdCo5cNi5—5c is shown to be consistent with a more constant Co moment over the region of composition compared with analog series. Exchange and crystal field (V) parameters are obtained from numerous Gd compounds, using the compensation points for the former and nuclear quadrupole interaction data for the latter. Within this framework, trends in intrinsic hardness can be better understood and new strategies for maximizing the effects become clearer. Einige Aspekte der intrinsischen Koerzivitat von Legierungsserien der Seltenen-Erd-Ubergangsmetalle werden insbesondere im Hinblick auf den Vergleich von relevanten Parametern zwischen Serien auf Gd-Grundlage mit Analogua auf Basis anisotroper Seltener Erden diskutiert. Insbesondere wird gezeigt, das das Fehlen der Tieftemperatur-Koerzitivitat in GdCo5cNi5—5c mit einem konstanteren Co-Moment uber den Zusammensetzungsbereich im Vergleich mit analogen Serien konsistent ist. Austausch- und Kristallfeld (V)-Parameter werden aus zahlreichen Gd-Verbindungen erhalten, wobei fur die ersteren die Kompensationspunkte und fur die letzteren die Werte fur die Kernquadrupolwechselwirkung benutzt werden. Innerhalb dieses Rahmens lassen sich die Tendenzen der intrinsischen Harte besser verstehen und neue Strategien fur eine Maximierung des Effekts werden klarer.